Фазовая диаграмма системы N-Zr

К оглавлению: Другие диаграммы (Others phase diargams)


In-Zr (Indium-Zirconium) H. Okamoto The assessed In-Zr phase diagram is tentative, because experimental information is scarce. The Zr-rich end (>75 at.% Zr) of the diagram is based on the studies of [58Bet2] and [59Lyu]. The melting reactions of intermediate compounds are probably not congruent type, because, according to the prediction of [69Das], In and Zr are immiscible in the liquid state. Addition of In to Zr stabilizes (aZr), as shown in the assessed diagram [ 58Bet1, 58Bet2, 62Uy]. The increase of the allotropic transformation temperature with increasing In content was calculated thermodynamically by [ 58Bet1]. The result was in qualitative agreement with the assessed diagram. InZr3 is not superconducting at 1.02 K [63Mat]. 58And: K. Anderko, Z. Metallkd., 49(4), 165-172 (1958) in German. 58Bet1: J.O. Betterton, Jr. and J.H. Fyre, Acta Metall., 6, 205-211 (1958). 58Bet2: J.O. Betterton, Jr. and W.K. Noyce, Trans. Metall. Soc. AIME, 212(6), 340-342 (1958). 59Lyu: B. Lyustman and F. Kerts, Metallurgy of Zirconium, 262 (1959) as quoted in [76Vol]. 62Sch: K. Schubert, H.G. Meissner, M. Potzschke, W. Rossteutscher, and E. Stolz, Naturwissenschaften, 49, 57 (1962). 62Uy: J.C. Uy and A.A. Burr, Trans. Metall. Soc. AIME, 224(2), 204 (1962). 63Mat: B.T. Matthias, T.H. Geballe, and V.B. Compton, Rev. Mod. Phys., 35(1), 1-22 (1963). 63Sch: K. Schubert, K. Frank, R. Gohle, A. Maldonado, H.G Meissner, A. Raman, and W. Rossteutscher, Naturwissenschaften, 50, 41 (1963). 64Sch: K. Schubert, H.G. Meisner, A. Raman, and W. Rossteuscher, Naturwissenschaften, 51, 287 (1964). 69Das: C. Dasarathy, Trans. Metall. Soc. AIME, 245(9), 2015-2019 (1969). 76Vol: A.E. Vol and I.K. Kagan, Handbook of Binary Metallic Systems, Vol. 3 ( 1976) in Rusian; translated by NBS/NSF, 682-684 (1985). Published in Bull. Alloy Phase Diagrams, 11(2), Apr 1990. Complete evaluation contains 1 figure, 2 tables, and 12 references. 1