Фазовая диаграмма системы Cu-Sb

К оглавлению: Другие диаграммы (Others phase diargams)

Cu-Sb

Cu-Sb (Copper-Antimony) Editor The assessed Cu-Sb phase diagram is drawn essentially from [Hansen] and [ Elliott], with minor modifications in the liquidus, solidus, and solvus boundaries. The liquidus is a composite of the data of [36Mur], [59Vec], [ 77Hay], and [83Heh], whereas the solidus of (Cu) is from [83Heh]. The solvus boundaries of (Cu) are drawn from [37Mer], [47Tar], and [58Raj]. The region between 18 and 30 at.% Sb is taken from [58Gun], and the b phase field is from [38Mur]. The solubility of Cu in (Sb) was determined to be negligible. -P.R.S. 36Mur: T. Murakami and N. Shibata, Sci. Rep. Tohoka Imp. Univ., 25, 527-568 ( 1936). 36Ela: M. Elander, G. Hagg, and A. Westgren, Ark. Kemi Min. Geol., 12B(1), 1 ( 1936). 37Mer: J.C. Mertz and C.H. Mathewson, Trans. AIME, 124, 59-77 (1937). 38Mur: T. Murakami and N. Shibata, Sci. Rep. Tohoku Imp. Univ., 27, 459-484 ( 1938). 40Age: N.V. Ageev and E.S. Makarov, Izv. Sektora Fiz. Khim. Anal., 13, 171-176 (1940). 41Hof: W. Hofmann, Z. Metallkd., 33, 373 (1941). 47Tar: V.P. Tarasova, Vestn. Mosk. Univ., 4, 105-107 (1947). 54Sch: K. Schubert and M. Ilschner, Z. Metallkd., 45, 366-370 (1954). 58Raj: B. Rajda, Hutn. Listy, 13, 761-768 (1958). 58Gun: E. Gunzel and K. Schubert, Z. Metallkd., 49, 124-133 (1958). 59Vec: A.A. Vecher and Y.I. Gerasimov, Nauchn. Dokl. Vysshei Shkoly, Khim. Khim. Tekhnol., 1, 16-18 (1959). 72Yam: S. Yamaguchi and M. Hirabayashi, J. Phys. Soc. Jpn., 33(3), 708-717 ( 1972). 77Hay: E. Hayer, K.L. Komarek, and R. Castanet, Z. Metallkd., 68(10), 688-696 ( 1977). 83Heh: T. Hehnkamp and R. Kossak, Z. Metallkd., 74(4), 195-198 (1983). 1