Фазовая диаграмма системы In-U

К оглавлению: Другие диаграммы (Others phase diargams)


In-U (Indium-Uranium) H. Okamoto The assessed phase diagram for the In-U system is based on the experimental data of [48Hay] and [63Joh]. It has been investigated only along the L/[L + In3U] liquidus. The AuCu3-type intermediate phase, In3U, is known to exist in this system. Its melting temperature and the type of melting are unknown. In3U is not superconducting at 0.07 K [70Hav]. [69Das] predicted the incidence of liquid immiscibility in the In-U system. No confirmation is available. The solubility of U in liquid In (L/[L + In3U]) was measured by [48Hay] and [ 63Joh]. The Arrhenius plot of the solubility data in the assessed diagram shows that the solubility of U observed by [48Hay] is about three times as much as that observed by [63Joh]. [63Joh] considered the larger apparent solubility of U observed by [48Hay] to be due to In3U crystals carried over into the unfiltered samples. [63Joh] expressed the liquidus as: log (at.% U) = 3.781 - 5146/T. 48Hay: E.E. Hayes and P. Gordon, USAEC Rep. TID-65, 130-141 (1948), quoted in [ Chiotti]. 52Ian: A. Iandelli, and R. Ferro, Ann. Chim. (Rome), 42, 598-608 (1952) in Italian. 53Fro: B.R.T. Frost and J.I. Maskrey, J. Inst. Met., 81/82, 171 (1953). 58Fer: R. Ferro, Acta Crystallogr., 11, 737-738 (1958). 63Joh: I. Johnson and M.G. Chasanov, Trans. ASM, 56, 272-277 (1963). 69Das: C. Dasarathy, Trans. Metall. Soc. AIME, 245(9), 2015-2019 (1969). 70Hav: E.E. Havinga, H. Damsma, and M.H. Van Maaren, J. Phys. Chem. Solids, 31, 2653-2662 (1970). 73Mur: A. Murasik, J. Leciejewicz, S. Ligenza, and A. Misiuk, Phys. Status Solidi (a), 20, 395-401 (1973). Submitted to the APD Program. Complete evaluation contains 1 figure, 3 tables, and 13 references. 1