Фазовая диаграмма системы In-Zn

К оглавлению: Другие диаграммы (Others phase diargams)

In-Zn

In-Zn (Indium-Zinc) J. Dutkiewicz and W. Zakulski The assessed In-Zn diagram is based primarily on the work of [44Rhi], [50Car], [56Oel], and [83Dut]. The liquidus on the Zn side of the eutectic was calculated, assuming the maximum solubility of In in (Zn) to be only 0.12 at.% In. Liquidus temperatures obtained from the thermodynamic properties are very close to the selected experimental values, with an average deviation of с6 K. [69Nis] showed primary Zn precipitates within a eutectic structure in a directionally solidified 4.8 at.% Zn alloy, which also indicates that the composition is hypereutectic. 44Rhi: F.N. Rhines and A. Grobe, Trans. AIME, 156, 253-262 (1944). 50Car: S.C. Carapella and E.A. Peretti, Trans. AIME, 188, 890-891 (1950). 56Oel: W. Oelsen and E.A. Zuhlke, Arch. Eisenhuttenwes., 27, 743-752 (1956) in German. 69Nis: G.S. Nishimura, R.S. Fidler, R.M. Taylor, and R.W. Smith, Can. Met. Q., 8, 319-322 (1969). 83Dut: J. Dutkiewicz and Z. Moser, Bull. Acad. Pol. Sci. Tech., 31, 27-30 ( 1983). Published in Bull. Alloy Phase Diagrams, 5(3), Jun 1984. Complete evaluation contains 4 figures, 5 tables, and 22 references. 1